OXIDIZED 90-25
General information:
- Oxidized bitumen can be produced by putting vacuum residue under the pressure and temperature between 200-300 centigrade degree. The result of oxidation hydrogen atoms of bitumen with oxygen of air lead to hydrocarbon polymerization reaction. The obtained bitumen after this process has lower penetration and higher softening point than the primary bitumen.
- Oxidized bitumen 90/25 is a semi-solid oxidized grade which is a straight run bitumen. It`s penetration is 25 and It`s softening point is 90 centigrade. The main applications of Oxidized bitumen 90/40 are bitumen coating, waterproof membrane, insulation and isolation industries and in road construction and asphalt paving.
- Packing: Bitumen supply is able to provide every packaging according to customers enquiry, including: Kraft bag, melt able plastic bag, drum
Technical Specifications:
. | Unit | Specification | Test method |
Specific gravity @25/25 C | (Kg/m3) | 1.05 approx. | ASTM D70 |
Penetration @ 25°c | mm/10 | 20/30 | ASTM D5 |
Softening point °c | °C | 90/100 | ASTM D36 |
Ductility @25 °c | Cm | 1.5 min | ASTM D113 |
Loss on heating(wt) % | Wt. % | 0.2 max | ASTM D6 |
Flashpoint c | °C | 230 min | ASTM D92 |
Solubility is CS2(wt) % | Wt. % | 99 min | ASTM D4 |
Spot test | - | Negative | A.A.S.H.O.T 102 |